ASTM A312 TP316L Seamless Stainless Steel Pipe
ASTM A312 / ASME SA312 is the standard specification for seamless, welded, and heavily cold-worked austenitic stainless steel pipes intended for high-temperature and general corrosive service.This standard is widely recognized and adopted globally, particularly in oil & gas, chemical processing, petrochemical, and industrial piping systems.
TP316L (Type 316L)is a low-carbon variant of the standard TP316 grade, identifiedUNS designation S31603
Chemical Composition:
Element | Weight % (ASTM A312 TP316L) |
Carbon (C) | ≤ 0.035% |
Manganese (Mn) | ≤ 2.00% |
Phosphorus (P) | ≤ 0.045% |
Sulfur (S) | ≤ 0.030% |
Silicon (Si) | ≤ 1.00% |
Chromium (Cr) | 16.00 - 18.00 per cent |
Nickel (Ni) | 10.00 - 14.00 per cent |
Molybdenum (Mo) | 2.00 - 3.00 per cent |
Nitrogen (N) | ≤ 0.10% |
The key distinction between TP316 and TP316L lies in carbon content: TP316 has a maximum of 0.08% C, while TP316L caps at 0.035% C. The lower carbon content eliminates carbide precipitation during welding, preventing intergranular corrosion in the heat-affected zone.
Mechanical Properties:
ASTM A312 TP316L seamless pipe exhibits excellent mechanical properties in the solution-annealed condition:
Property | Value |
Tensile Strength | ≥ 485 MPa (70 ksi) min |
Yield Strength (0.2% offset) | ≥ 170 MPa (25 ksi) min |
Elongation | ≥ 35% min |
Hardness (Brinell HBW) | ≤ 217 max |
Hardness (Rockwell B HRB) | ≤ 95 max |
Density | 7.98 g/cm³ |
Melting Point | 1375 - 1450°C |
ASTM A312 TP316L is recognized globally under various national standards:
Standard | Country/Region | Equivalent Grade |
ASTM A312 | United States | TP316L (UNS S31603) |
EN 10088-2 | Europe | 1.4404 / X2CrNiMo17-12-2 |
GB/T 20878 | China | 022 Cr17Ni12Mo2 |
JIS G3459 | Japan | SUS316L |
DIN 17440 | Germany | X2CrNiMo17-12-2 |
BS 970 | United Kingdom | 316S11 |
ISO 683/13 | International | 316L |
Property | TP316L | TP316 |
|---|---|---|
Carbon | ≤ 0.035% | ≤ 0.08% |
Tensile Strength | ≥ 485MPa | ≥ 515MPa |
Yield Strength | ≥ 170MPa | ≥ 205MPa |
Corrosion After Welding | Excellent | Good (may need PWHT) |
Main Use | Welded systems, critical corrosion | Non-welded, higher strength |
Parameter Range:
Nominal Pipe Size (NPS) 1/8″ to 48 ″
Outside Diameter (OD) 6.35mm to 1219mm
Wall Thickness SCH 5S to SCH XXS
Length Single random, double random, or fixed cut length
End Connections Plain End (PE) or Beveled End (BE)
Applications & End-Use Industries
ASTM A312 TP316L seamless pipes are widely used across demanding industries where corrosion resistance, cleanliness, and reliability are critical:
Industry | Typical Applications |
Chemical & Petrochemical | Process piping, reactors, heat exchangers, corrosive chemical handling-2 |
Oil & Gas | Offshore pipelines, refineries, high-pressure gas transmission, sour service- |
Marine & Offshore | Seawater systems, shipbuilding, offshore platforms, desalination plants-4 |
Food & Beverage | Sanitary piping, processing equipment, dairy, breweries- |
Pharmaceutical | Cleanroom piping, biopharmaceutical processing, ultra-pure water systems- |
Power Generation | Heat exchangers, boiler components, condenser tubes |
Pulp & Paper | Bleaching plants, chemical recovery systems- |
Aerospace & Biomedical | Hydraulic systems, surgical instruments, implants, diagnostic devices |
fAQ
1. Are we do producer or trader?
For stainless steel,we are do trading
2. What is our payment terms?
a. 30% TT in advance+70% TT before shipping after inspection
B .30% TT in advance+70% LC at sight
3. What certiifcates we can provide?
SGS;TUV;BV; Mill Test Certificate